Nodweddion Cynnyrch:
Mae gan ein gwifren gyda Ni10% BZN 10-25 ymwrthedd cyrydiad cryf, hydwythedd uchel, cryfder cymedrol neu uwch, prosesu a ffurfioldeb da, a weldadwyedd.
Manylebau:
|
Freg |
Bzn 10 - 25 |
|
ASTM |
Na |
|
En |
Na |
|
Jis |
C7541 |
Cyfansoddiad cemegol (pwysau%):
|
Cu |
63.5 - 66.5 |
|
NI + CO |
9.0 - 110 |
|
Fefau |
Llai na neu'n hafal i 0.2 |
|
PB |
Llai na neu'n hafal i 0.09 |
|
Mn |
Llai na neu'n hafal i 0.5 |
|
P |
Llai na neu'n hafal i 0.005 |
|
Zn |
Gweddillion |
Ceisiadau Diwydiannol:
Priodweddau Ffisegol:
|
Ddwysedd |
8.94 |
g/cm3 |
|
Dargludedd @ 20 gradd |
9.1 |
%Iacs |
|
Dargludedd @ 20 gradd |
190 |
MS/M. |
|
Dargludedd thermol@20 gradd |
40 |
W/(m⋅K) |
|
Capasiti gwres penodol |
380 |
/J. (kg.∘c) .t |
|
Modwlws elastig |
120 |
MPa |
|
Cymhareb Poisson |
140 |
GPA |
|
Cyfernod ehangu thermol |
16.4 |
10-6/K |
Priodweddau Mecanyddol:
|
Ngwladwriaeth |
Cryfder tynnol |
Cryfder Cynnyrch |
Caledwch |
Cyfradd |
||
|
mm |
MPa |
ksi |
MPa |
HV |
A₅₀% |
|
|
Φ0.1 - 0.2 |
60 |
375 |
54 |
-- |
127 |
Yn fwy na neu'n hafal i 18 |
|
＞Φ0.2 - 0.5 |
60 |
355 |
51 |
-- |
112 |
Yn fwy na neu'n hafal i 25 |
|
＞Φ0.5 - 2.0 |
60 |
335 |
49 |
-- |
105 |
Yn fwy na neu'n hafal i 30 |
|
＞Φ2.0 - 8.0 |
60 |
275 |
40 |
-- |
87 |
Yn fwy na neu'n hafal i 35 |
|
Φ0.1 - 0.2 |
H01 |
400 |
58 |
-- |
125 |
Yn fwy na neu'n hafal i 10 |
|
＞Φ0.2 - 0.5 |
H01 |
380 |
55 |
-- |
120 |
Yn fwy na neu'n hafal i 15 |
|
＞Φ0.5 - 2.0 |
H01 |
370 |
54 |
-- |
115 |
Yn fwy na neu'n hafal i 20 |
|
＞Φ2.0 - 8.0 |
H01 |
330 |
48 |
-- |
103 |
Yn fwy na neu'n hafal i 25 |
|
Φ0.1 - 0.2 |
H02 |
410 |
59 |
-- |
127 |
-- |
|
＞Φ0.2 - 0.5 |
H02 |
390 |
57 |
-- |
123 |
Yn fwy na neu'n hafal i 5 |
|
＞Φ0.5 - 2.0 |
H02 |
375 |
54 |
-- |
117 |
Yn fwy na neu'n hafal i 10 |
|
＞Φ2.0 - 8.0 |
H02 |
340 |
49 |
-- |
107 |
Yn fwy na neu'n hafal i 12 |
|
Φ0.1 - 0.2 |
H03 |
540 - 735 |
78 - 107 |
-- |
168 - 228 |
-- |
|
＞Φ0.2 - 0.5 |
H03 |
490 - 685 |
71 - 99 |
-- |
155 - 213 |
-- |
|
＞Φ0.5 - 2.0 |
H03 |
440 - 635 |
64 - 92 |
-- |
137 - 198 |
-- |
|
＞Φ2.0 - 8.0 |
H03 |
340 - 520 |
49 - 75 |
-- |
107-163 |
|
Goddefgarwch:
|
Fanylebau |
Oddefgarwch |
Hyd gwialen syth |
|||
|
mm |
gwifren (mm) |
gwialen |
fanylebau |
hyd (m) |
goddefgarwch hyd (mm) |
|
0.3 - 1.0 |
0.01 |
-- |
-- |
-- |
-- |
|
＞1.0 - 2.0 |
0.02 |
0.02 |
1.5 - ＜1.8 |
0.5 - 1.0 |
± 10mm |
|
＞2.0 - 4.0 |
0.02 |
0.03 |
1.8 - 2.5 |
0.5 - 2.0 |
± 10mm |
|
＞Φ4.0 - 6.0 |
0.03 |
0.04 |
＞2.5 - 5.0 |
1.0 - 2.5 |
± 10mm |
|
＞6.0 - 9.0 |
0.03 |
0.04 |
＞5.0 - 9.0 |
1.0 - 2.5 |
± 10mm |
|
＞9.0 - 12.0 |
0.04 |
0.05 |
＞9.0 |
2.0 - 3.0 |
± 10mm |
Dull Cyflenwi:
|
Fanylebau |
Pwysau rholio safonol |
Rholio diamedr mewnol |
|
mm |
kg |
mm |
|
2.8 - 6.5 |
30 - 45 |
370 - 400 |
|
4.0 - 6.5 |
100 - 250 |
400 - 650 |
|
6.5 - 10.0 |
50 - 100 |
400 - 650 |
|
Fanylebau |
Pwysau rholio safonol |
Rholio diamedr mewnol |
|
mm |
kg |
mm |
|
2.8 - 6.5 |
30 - 45 |
370 - 400 |
|
4.0 - 6.5 |
100 - 250 |
400 - 650 |
|
6.5 - 10.0 |
50 - 100 |
400 - 650 |